Normally, the tungsten alloy rod after swaging, ultimate tensile strength would be increased quitely. The ultimate tensile strength of general tungsten alloy rod is 1050 MPa . However, after swaging, the ultimate tensile strength can be up to 1200 MPa min, we could even control at 1400 MPa. This type of rod is one of our main products. The composition of this kind of products is 93%WNiFe. Following are our common types of tungsten alloy swaging rod:
Diameter: 12mm~20mm, Length: less than 400mm;
Diameter: 20mm~400mm, Length: less than 500mm.
As well, we can produce the products according to the clients' demand
Application of tungsten alloy swaging rod on the Military field:
Tungsten alloy swaging rod can be widely use in military defense, such as depleted uranium penetrators, bullet, armor piercing, rifle bullet, snipe rifle penetrator, etc.
Process of tungsten alloy swaging rod:
1). Mixing
2). Pressing
3). Sintering
4). Heat treatment
5). Swaging
6). Machining